主題 EXPERIMENTAL STUDY ON DRYING SHRINKAGE CRACKING CHARACTERISTICS OF STEEL CHIP REINFORCED POLYMER CEMENTITIOUS COMPOSITE
副題
筆頭著者 洪善熙(京都大学)
連名者1 木村真也(京都大学)
連名者2 佐藤裕一(京都大学)
連名者3 金子佳生(京都大学)
連名者4
連名者5
キーワード drying shrinkage、fiber reinforced cementitious composite、polymer、reuse、steel chip、スチル―チップ、ポリマー、乾燥収縮、再利用、繊維補強セメント系複合材料
36
1
先頭ページ 460
末尾ページ 465
年度 2014
要旨 This study is to clarify the drying shrinkage and shrinkage cracking characteristics of steel chip reinforced polymer cementitious composite (SCRPCC). In this study, free shrinkage of SCRPCC, drying shrinkage and shrinkage cracking of SCRPCC reinforced with deformed bars were examined. Test results shows that (1) the free shrinkage of SCRPCC is smaller than that of polymer cement mortar (PCM) at the outside; (2) the restrained shrinkage of PCM specimens was reduced by reinforcing with steel chip; (3) average crack width of PCM specimen with low reinforcement ratio was greatly declined by reinforcing with steel chip.
PDFファイル名 036-01-1070.pdf


検索結果へ戻る】 【検索画面へ戻る