| 種別 | 論文 |
| 主題 | Effect of Alkaline Activator and Curing Method on the Compressive Strength of Cementless Fly Ash Based Alkali-Activated Mortar |
| 副題 | |
| 筆頭著者 | Gyung-Taek KOH（Korea Institute of Construction Technology） |
| 連名者1 | Hyun Jin KANG（Korea Institute of Construction Technology） |
| 連名者2 | Gum Sung RYU（Korea Institute of Construction Technology） |
| 連名者3 | Jang Hwa LEE（Korea Institute of Construction Technology） |
| 連名者4 | |
| 連名者5〜 | |
| キーワード | fly ash、alkali-activated mortar、compressive strength、curing method、alkaline activator、fly ash、alkali-activated mortar、compressive strength、curing method、alkaline activator |
| 巻 | 31 |
| 号 | 1 |
| 先頭ページ | 2209 |
| 末尾ページ | 2214 |
| 年度 | 2009 |
| 要旨 | This study investigates the effects of alkaline activator and curing method on the compressive strength of mortar for the development of cementless alkali-activated concrete using 100% of fly ash as binder. Results reveal that alkali-activated mortar with compressive strength of 70MPa at age 28 days can be fabricated in case of performing atmospheric curing after curing at 60°C during 48 hours when using alkaline activator made of NaOH of 9M and sodium silicate with proportions of 1:1. |
| PDFファイル名 | 031-01-1362.pdf |