| 種別 | 論文 |
| 主題 | 鉄筋腐食によるひびわれ進展挙動の定量的評価解析 |
| 副題 | |
| 筆頭著者 | Khoa Kim TRAN（Nagoya University） |
| 連名者1 | 中村光（名古屋大学） |
| 連名者2 | 河村圭亮（名古屋大学） |
| 連名者3 | 国枝稔（名古屋大学） |
| 連名者4 | |
| 連名者5〜 | |
| キーワード | 剛体ばねモデル、局部的腐食、腐食の侵入、膨張モデル、ひび割れ幅、内部ひびわれ、Rigid Body Spring Model、Local Corrosion、Penetration of corrosion products、Expansion Model、Crack Width、Internal Crack |
| 巻 | 32 |
| 号 | 1 |
| 先頭ページ | 1043 |
| 末尾ページ | 1048 |
| 年度 | 2010 |
| 要旨 | Cracking behavior due to rebar corrosion for concrete specimen with single rebar was evaluated analytically. The evaluation was performed by comparing with results of the electric corrosion test. Three-dimensional Rigid- Body-Spring-Method (RBSM) with three phase material corrosion expansion model was applied to simulate internal cracking patterns and surface crack width propagation. The effect of rebar local corrosion and penetration of corrosion products into cracks during the corrosion process were investigated and cracking behavior due to rebar corrosion was evaluated quantitatively. |
| PDFファイル名 | 032-01-1166.pdf |