| 主題 | INFLUENCE OF SLAG ON MECHANICAL PROPERTIES AND DURABILITY OF SHIRASU GEOPOLYMER |
| 副題 | |
| 筆頭著者 | Katpady Dhruva Narayana（Kagoshima University） |
| 連名者1 | 武若耕司（鹿児島大学） |
| 連名者2 | 山口明伸（鹿児島大学） |
| 連名者3 | 審良善和（鹿児島大学） |
| 連名者4 | |
| 連名者5 | |
| キーワード | acid resistance, alkali activators, compressive strength, geopolymer, GGBS, shirasu, アルカリ活性剤, ジオポリマー, シラス, 圧縮強度, 耐酸性, 高炉スラグ |
| 巻 | 39 |
| 号 | 1 |
| 先頭ページ | 2113 |
| 末尾ページ | 2118 |
| 年度 | 2017 |
| 要旨 | Shirasu, a pyroclastic flow deposit, is used as aluminosilicate in producing geopolymer. Ground granulated blast furnace slag is used as an admixture for development of higher initial strength of Shirasu geopolymer. Sodium hydroxide and sodium silicate solution are used as alkaline activators. Mortars are atmospheric cured or oven dry heat cured for 24 hours. Compressive strength and sulfuric acid immersion tests are carried out. Based on the experimental study, it was observed that the initial and long term strength development of Slag-Shirasu geopolymer improved and acid resistance increased. |
| PDFファイル名 | 039-01-1345.pdf |