主題 WORKABILITY AND COMPRESSIVE STRENGTH OF Na2SiO3-ACTIVATED GEOPOLYMER MORTAR CURED AT AMBIENT TEMPERATURE
副題
筆頭著者 Shaoqi HUANG(Kyoto University)
連名者1 Yukun ZHANG(Kyoto University)
連名者2 Yihan BAI(Kyoto University)
連名者3 Lin AN(Kyoto University)
連名者4
連名者5
キーワード cylinder compressive strength、Na2SiO3-activated geopolymer mortar、S/N analysis、S/N分析法、Taguchi array、workability、ケイ酸ナトリウムで活性化されたジオポリマーモルタル、タグチメソッド、ワーカビリティ
41
1
先頭ページ 2003
末尾ページ 2008
年度 2019
要旨 This study aims to investigate the most influential factors which dominant the flow ability, setting time and compressive strength of Na2SiO3-activated geopolymer mortar cured at ambient temperature. The factors include sodium silicate concentration, alkaline activator-to-binder ratio and slag content. A Taguchi orthogonal array was adopted to conduct the experiment and the S/N analysis was used to evaluate the significance of factors. Results show that sodium silicates concentration plays the most vital role on both workability and compressive strength among these above factors.
PDFファイル名 041-01-1329.pdf


検索結果へ戻る】 【検索画面へ戻る